Effect of Cold Rolling on Microstructure and Mechanical Properties of AISI 301LN Metastable Austenitic Stainless Steels

查看全文 作　　者：HUANG Jun-xia1, YE Xiao-ning1, XU Zhou2 (1. Shanghai Baosteel Research Institute, Shanghai 200431, China;2. School of Material Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240, China)

出　　处：《Journal of Iron and Steel Research(International)》索引2012年第19卷第10期,共5页

基　　金：Item Sponsored by National High-Tech Research and Development Program (863 Program) of China (2008AA030702) 摘　　要：The microstructure and mechanical properties evolution of AISI 301LN metastable austenitic stainless steels during cold rolling were investigated. A wide range of cold thickness reduction (10%-80%) was carried out in a four-high rolling mill at ambient temperature. The X-ray and Feritscope MP30 were used to identify the strain-induced α′-martensite phase and its volume fraction, respectively. The microstructure was observed by optical micrograph and the mechanical properties were determined by tensile tests and microhardness. The results show that the strain-induced α′-martensite nucleated at the shear bands intersections and the growth of α′-martensite occurred by the repeated nucleation of new embryos. The volume fraction of strain-induced α′-martensite increased with increasing the cold rolling reduction. In addition, the percentage increased in the tensile strength is the same as that of hardness. The ratio between the average tensile strength and the average microhardness was found to range between 2.82 and 3.17. 关键词：METASTABLE AUSTENITIC STAINLESS steel cold ROLLING reduction strength

相关文献

参考文献（17）
引证文献（10）
耦合文献（0）

参考文献(17)

引证文献(10)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Effect of Cold Rolling on Microstructure and Mechanical Properties of AISI 301LN Metastable Austenitic Stainless Steels

参考文献(17)

引证文献(10)

用户提示