共被期刊论文引用了3次
您的检索式：您选中1篇文献正在查看引证文献汇总
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | 304不锈钢点蚀行为的电化学阻抗谱研究显示文摘综合运用动电位电化学阻抗谱(DEIS)和时间扫描模式下的电化学阻抗谱(TSEIS)研究了304不锈钢在3.5%(质量分数)NaCl溶液中的点蚀行为。DEIS的结果表明,在比点蚀电位0.15V负得多的电位0.02V下,亚稳态点蚀就已经开始,并且亚稳态蚀孔的产生与再钝化是随机的,DEIS测试得到的稳态点蚀电位比动电位极化法得到的点蚀破裂电位要负0.05V。TSEIS的结果表明,只有在钝化膜减薄到一定程度后,点蚀的形核才能发生。通过对等效电路中元件参数的分析,揭示了点蚀发展过程中双电层和钝化膜结构的变化特点。 | 杜楠 叶超 田文明 赵晴 | 2014 | 材料工程2014，42，6： | 46 |
| 2 | Corrosion behavior of 2195 and 1420 Al-Li alloys in neutral 3.5% NaCl solution under tensile stress显示文摘The corrosion behaviors of 1420 and 2195 Al-Li alloys under 308 and 490 MPa tensile stress respectively in neutral 3.5% NaCl solution were investigated using electrochemical impedance spectroscopy(EIS) and scanning electron microscope(SEM). It is found that the unstressed 1420 alloy is featured with large and discrete pits, while general corrosion and localized corrosion including intergranular corrosion and pitting corrosion occur on the unstressed 2195 alloy. As stress is applied to 1420 alloy, the pit becomes denser and its size is decreased. While, for the stressed 2195 alloy, intergranular corrosion is greatly aggravated and severe general corrosion is developed from connected pits. The EIS analysis shows that more severe general corrosion and localized corrosion occur on the stressed 2195 Al-Li alloy than on 1420 Al-Li alloy. It is suggested that tensile stress has greater effect on the corrosion of 2195 Al-Li alloy than on 1420 Al-Li alloy. | 李劲风 陈文敬 赵旭山 任文达 郑子樵 | 2006 | 中国有色金属学会会刊:英文版2006，16，5： | 9 |
| 3 | 温度对粉土电化学特性影响的试验研究显示文摘为了研究不同温度下粉土电化学性质的变化规律,通过使用电化学法测量粉土在五个温度梯度下的电化学阻抗谱图,运用Zsim Demo拟合其等效电路,研究电路参数的变化规律及分析其机理,结果表明:温度对粉土Nyquist图影响表现为高频区和中频区的两个时间常数下的圆弧以及低频区的扩散斜线;Bode图表现为随着温度的上升,土的阻抗模值持续减小;不同温度所对应的实际等效电路包含了溶液电阻、电荷传递电阻、常相位角元件、多孔层的电阻元件、电容元件以及扩散电阻六个电化学元件;随着温度的升高,电极发生反应的速率随之增快,电荷在土中的导体相转移速度增快,表现出溶液电阻、电荷传递电阻、多孔层的电阻均在-20℃时最大,而常相位角原件的双电层电容参数值在20℃时达到最大。 | 郝钰 韩鹏举 何斌 | 2018 | 科学技术与工程2018，18，19： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员