| 1 | Investigation of carbon contamination in lost foam castings of low carbon steel显示文摘Lost foam casting(LFC) process is a special casting method in which polymeric foam patterns with refractory coatings are utilized as a mould component. In this work, four types of foam: expandable polyethylene(EPE), expandable polypropylene(EPP) and expandable polystyrene(EPS) foams with two different densities were employed as pattern materials. LFC and conventional green sand mould casting methods were used to cast a low carbon steel, A216 Grade WCB. Both casting processes were carried out at 1,580 °C. Chemical analysis results showed that the carbon contamination level was high and was influenced by pattern type. Metallographic investigations revealed a significant increase in the percentage of pearlite phase in all LFC samples. Densities of manufactured samples were calculated in order to evaluate porosity of the products. It was determined that the densities of the LFC samples were lower than the green sand mould cast reference sample(RS). Vickers hardness tests were also carried out and increments in hardness values with increased carbon content was observed. | Oznur Kilic Serhat Acar Alptekin Kisasoz Kerem Altug Guler | 2018 | China Foundry2018，15，5： | 2 |
| 2 | T6热处理对触变锻造加低过热铸造制备的A356和A380铝合金的影响(英文)显示文摘研究T6热处理对触变锻造A356和A380铝合金的影响。采用低过热铸造(LSC)技术制备用于触变锻造的样品。为了获得等轴晶粒并防止枝晶生长,将样品在高于液相温度20°C时进行浇铸,将浇铸坯料再加热不同时间(20~80 min)后进行触变锻造,变形量为50%,再将触变锻造后的A356和A380铝合金样品进行T6热处理。用光学显微镜、能量弥散X射线谱仪、扫描电镜和布氏硬度仪对经触变锻造、固溶处理和时效处理后样品的显微组织和硬度变化进行检测。结果表明,T6热处理后合金的显微组织更均匀,并分别在A356和A380坯料中形成了新的析出相Mg_2Si和Al_2Cu。相应地,经过人工时效后,样品的硬度大幅度提高,A356铝合金的硬度达到HB 93,A380铝合金的硬度达到HB 120。 | Ridvan GECU Serhat ACAR Alptekin KISASOZ Kerem ALTUG GULER Ahmet KARAASLAN | 2018 | Transactions of Nonferrous Metals Society of China2018，28，3： | 2 |
您所在的机构暂未开通此部分的功能，请联系管理员