共被期刊论文引用了3次
您的检索式：您选中1篇文献正在查看引证文献汇总
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | 表面涂覆含氟羟基磷灰石和缺钙羟基磷灰石的镁合金体外降解行为(英文)显示文摘通过电化学沉积方法,在生物降解镁合金表面覆盖含氟羟基磷灰石(FHA)涂层和缺钙羟基磷灰石(CDHA)涂层。采用X射线衍射、傅立叶变换红外光谱、透射电子显微镜、扫描电子显微镜和能量色散X射线光谱研究涂层特性。结果表明:涂覆纳米FHA涂层的样品具有垂直于样品表面的纳米针状结构,比涂覆CDHA涂层样品的结构更致密和更均匀。纳米FHA涂层比纳米CDHA涂层具有更小的晶粒尺寸,分别为65 nm和95 nm。然而,CDHA涂层比FHA涂层更厚,厚度分别为19μm和15μm。通过极化、浸泡和析氢实验研究的腐蚀行为表明:纳米FHA涂层和纳米CDHA涂层显著降低腐蚀速率并引起钝化。纳米FHA和纳米CDHA涂层可以加速骨状磷灰石层的形成,相比未覆盖的镁合金可以显著减少溶出速率。纳米FHA涂层能对镁合金提供有效的防护并具有更高的腐蚀性能。因此,覆盖纳米FHA涂层的镁合金在整形外科领域具有良好的应用前景。 | H.R.BAKHSHESHI-RAD E.HAMZAH M.DAROONPARVAR M.A.M.YAJID M.KASIRI-ASGARANI M.R.ABDUL-KADIR M.MEDRAJ | 2014 | Transactions of Nonferrous Metals Society of China2014，24，8： | 3 |
| 2 | Characterization of mechanothermal-synthesized hydroxyapatite-magnesium titanate composite nanopowders显示文摘Hydroxyapatite-magnesium titanate composite nanopowders have been developed using a mechanothermal process.Thermal treatment of the milled powders at 700℃resulted in the formation of HAp/MgTiO_(3)-MgO nanocomposite.X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),and energy dispersive X-ray spectroscopy(EDX)techniques were utilized to characterize the synthesized powders.The results revealed that the dominant phases after mechanical activation were hydroxyapatite,anatase(TiO_(2))and periclase(MgO);while after thermal annealing process at 700℃,hydroxyapatite along with geikielite(MgTiO_(3))and periclase(MgO)were the major phases.Based on the XRD analysis,the evaluation of structural features of the samples indicated that the average crystallite sizes of hydroxyapatite after 10 h of milling and subsequent thermal treatment at 700℃were about 21 nm and 34 nm,respectively.Microscopic observations illustrated that the synthesized powders contained large agglomerates which consisted of significantly finer particles with spheroidal morphology.It is concluded that the mechanothermal method can be used to produce hydroxyapatite-based nanocomposite with appropriate structural and morphological features. | Abbas FAHAMI Bahman NASIRI-TABRIZI | 2013 | Journal of Advanced Ceramics2013，2，1： | 0 |
| 3 | Thermal treatment effect on structural features of mechano-synthesized fluorapatite-titania nanocomposite: A comparative study显示文摘The influence of thermal treatment on the structural features of mechano-synthesized fluorapatite-titania composite nanopowders was studied.A mixture of calcium and phosphate reagents was mixed with a certain amount of titania(20 wt%)and then was mechanically activated for 5 h,10 h and 15 h respectively.After that,the mechano-synthesized powders were annealed at 700℃for 2 h.The crystallite size of the composite nanopowders estimated from Williamson-Hall method was in good agreement with transmission electron microscopy(TEM)analysis.Scanning electron microscopy(SEM)/TEM images confirmed the formation of a cluster-like composite which was composed of ellipse-like nanoparticles with an average size of about 16±7 nm after 15 h of milling.During the milling process,large variations in mechanochemical behavior of the CaHPO_(4)-Ca(OH)_(2)-CaF2-TiO_(2) system were detected.After the beginning of milling,no trace of the composite was found due to the lack of sufficient time for the mechanical activation.When the mechanical activation time increased to 15 h,composite nanopowders with the crystallite size of around 21.66 nm were formed.During heating at 700℃,the recovery of crystallinity occurred and the fraction of crystalline phase reached a maximum around 88.79%for the 10-h milled sample.Results indicated that the structural features of the composite were strongly influenced by the subsequent annealing. | Bahman NASIRI-TABRIZI | 2014 | Journal of Advanced Ceramics2014，3，1： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员