题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Effects of Rhenium on Creep Rupture Life of a Single Crystal Superalloys显示文摘The slabs of a single crystal superalloy were poured with 2.2% Re, 3.2% Re and 4.2% Re and otherelement contents of the alloys were basicalIy kept no changed. The effects of Re on the ultimatetensile strength, creep rupture life and rafting of a single crystal superalloy were studied. Theresults showed that with increasing Re content the ultimate tensile strength decreased but theplasticity increased at 649℃. and the creep rupture life remarkably increased while the plasticitydecreased at 982℃/248.2 MPa. 1038℃/206.8 MPa and 1070℃/176.8 MPa for the alloy, on themicrostructure aspect, with increasing the creep rupture life of the alloy the rafting was gettingbigger and bigger at the same test condition, and the rafting suppressed creep and increasedcreep rupture life in this single crystal superalloy. | Li, Jiarong Tang, Dingzhong Lao, Riling Liu, Shizhong Wu, Zhongtang
| 1999 | Journal of Materials Science & Technology1999，15，1： | 8 |
您所在的机构暂未开通此部分的功能，请联系管理员